- 耐高溫，高阻燃
- 耐磨損
- 在高溫下耐腐蝕
- 徑向收縮比：2:1，軸向收縮率≤10%
- 收縮溫度：開始收縮溫度110 ℃，完全收縮溫度200 ℃
- 工作溫度：-55 ℃~200 ℃
- 管體柔韌
|
應用
高溫有油環(huán)境電子元件的保護；電阻電容器、熱電偶的絕緣及保護；各種金屬線類的機械保護；電線末端、接續(xù)、端子的絕緣、保護和補強。中科英華(原長春熱縮)系直九標準推薦生產(chǎn)廠家
| 技術指標 |
| 項目 |
|
性能 |
|
指標
|
|
典型值
|
|
測試標準
|
| |
|
|
|
|
|
|
|
|
| |
| |
| 機械性能 |
|
拉伸強度 |
|
>12MPa
|
|
>12MPa
|
|
ASTM D2671
|
| |
|
|
|
|
|
|
|
| |
斷裂伸長率 |
|
≥250%
|
|
430%
|
|
ASTM D2671
|
| |
|
|
|
|
|
|
|
| |
老化后斷裂伸長率(250 ℃ /168hrs) |
|
≥200%
|
|
250%
|
|
ASTM D2671
|
| |
|
|
|
|
|
|
|
| |
熱沖擊 (300 ℃ /4hrs) |
|
pass
|
|
no dripping
|
|
ASTM D2671
|
| |
|
| |
低溫柔韌性 (-55 ℃ /4hr) |
|
pass
|
|
Pass
|
|
ASTM D2671
|
| |
| 電性能 |
|
介電強度 |
|
>25kV/mm
|
|
>25kV/mm
|
|
ASTM D2671
|
| |
|
| |
體積電阻率 |
|
>1014Ω.cm
|
|
>1016Ω.cm
|
|
ASTM D 257
|
| |
| 化學性能 |
|
銅腐蝕 (250 ℃ /168hrs) |
|
No Corrosion
|
|
Pass
|
|
ASTM D2671
|
| |
|
| |
銅穩(wěn)定 (121 ℃ /168hrs) |
|
Elongation>70%
|
|
pass
|
|
UL 224
|
| |
|
| |
阻燃性能 |
|
|
|
Highly Flame Retardant
|
|
ASTM D2671
|
| |
|
|
|
|
|
|
|
| |
吸水率 |
|
<0.5%
|
|
<0.5%
|
|
ASTM D570
|
| |
|
| |
抗真菌性 |
|
|
|
Very Good
|
|
ISO 846
|
|
| 規(guī)格尺寸 |
| |
|
規(guī)格
|
內(nèi)徑
|
完全收縮后平均壁厚
|
| |
|
收縮前最小內(nèi)徑
|
收縮后最大內(nèi)徑
|
| |
|
mm
|
inch
|
mm
|
inch
|
mm
|
inch
|
mm
|
inch
|
| |
|
|
|
|
|
|
|
|
1.2
|
3/64
|
1.20
|
0.047
|
0.60
|
0.024
|
0.25±0.1
|
0.010±0.004
|
| |
|
1.6
|
1/16
|
1.60
|
0.063
|
0.80
|
0.032
|
0.25±0.1
|
0.010±0.004
|
| |
|
2.4
|
3/32
|
2.40
|
0.094
|
1.20
|
0.047
|
0.25±0.1
|
0.010±0.004
|
| |
|
3.2
|
1/8
|
3.20
|
0.126
|
1.60
|
0.063
|
0.25±0.1
|
0.010±0.004
|
| |
|
4.8
|
3/16
|
4.80
|
0.189
|
2.40
|
0.095
|
0.30±0.1
|
0.012±0.004
|
| |
|
6.4
|
1/4
|
6.40
|
0.252
|
3.20
|
0.126
|
0.30±0.1
|
0.012±0.004
|
| |
|
9.6
|
3/8
|
9.60
|
0.378
|
4.80
|
0.189
|
0.30±0.1
|
0.012±0.004
|
| |
|
12.8
|
1/2
|
12.80
|
0.504
|
6.40
|
0.252
|
0.30±0.1
|
0.012±0.004
|
| |
|
19
|
3/4
|
19.00
|
0.748
|
9.50
|
0.374
|
0.40±0.1
|
0.016±0.004
|
| |
|
25.4
|
1
|
25.40
|
1.000
|
12.70
|
0.500
|
0.50±0.1
|
0.020±0.004
|
| |
|
38
|
1 1/2
|
38.00
|
1.496
|
19.00
|
0.748
|
0.50±0.1
|
0.020±0.004
|
|