PC 1301EP-30
特性: 超低粘,脫模良好
應(yīng)用: 光碟安全盒,包裝用品,手機鍵區(qū),薄壁制品等
1301EP-30
測試項目 測試方法 單位 數(shù)值
Melt Flow Rate(300℃/1.2kg) ASTM D1238 g/10min 30
Density ASTM D792 1.2
Mold Shrinkage ASTM D955 mm/mm 0.005-0.007
Water Absorption@24hrs,23℃ ASTM D570 % 0.15
@equilibrium,50%RH,23℃ ASTM D570 % 0.32
Refractive index,no ASTM D542 1.586
Light Transmittance ASTM D1003 % 89
Haze ASTM D1003 % 0.7-1.5
Deflection Temperature Under Load(DTUL)@4mm ASTM D648 ℃
@66 psi(0.45MPa),annealed ASTM D648 ℃ 139
@264 psi(1.8MPa),annealed ASTM D648 ℃ 136
@264 psi(1.8MPa),unannealed ASTM D648 ℃ 122
Vicat Softening Point,50℃/hr,50N Load ASTM D1525 ℃ 144
Coefficient of Linear Thermal Expansion,@-40 to 82℃ ASTM D696 mm/mm/℃ 68×10-6
Tensile Yield Strength ASTM D638 Mpa 60
Ultimate Tensile Strength ASTM D638 Mpa 61
Elongation at Yield ASTM D638 % 6
Elongation at Break ASTM D638 % 150
Tensile Modulus ASTM D638 Mpa 2340
Flexural Strength ASTM D790 Mpa 96
Flexural Modulus ASTM D790 Mpa 2410
Notched Izod Impact @23℃ ASTM D256 J/m 700
Unnotched Izod Impact @23℃ ASTM D256 No break
Instrumented Dart Impact,Total Energy @23℃ ASTM D3763 J -
Rockwell Hardness ASTM D785 M Scale -
Taber Abrasion Resistance (△Haze) ASTM D1044 % -
UL-94 @0.5mm ASTM D635 V-2
UL-94 @1.6mm ASTM D635 V-2
UL-94 @2.5-2.7mm ASTM D635 V-2
UL-94 @3.0mm ASTM D635 HB
Limiting Oxygen Index ASTM D2863 % 26
Ball Indentation Temperature IEC598-1 ℃ >125
Average Extent of Burning ASTM D635 mm 25
GWT2.0mm,5second IEC695-2-1 ℃ 850
Comparative Tracking Index@2.0mm IEC112 V 250
Dielectric Strength ASTM D149 kv/mm 17
Eielectric Constant @60Hz ASTM D150 3
Dissipation Factor@60Hz ASTM D150 0.001
Volume Resistivity @23℃,dry ASTM D257 Ω-cm 2.0×1017